atomization testers are suitable for interior materials such as cars, aircrafts and other interior materials, such as car interior plastic parts, polyurethane, textiles, leather, adhesives, non -weaving cloth, thermal plastic elastic body and other materials Evaluation of the situation.
Testing principle:
The sample is heated in the fog cup and began to volatilize. The volatile gas condenses on the glass plate or aluminum foil that has been cooled by the cooling cavity. After the condensation process is over, remove the glass plate or aluminum foil, and measure the atomization value or weight of the condensation ingredients of the glass plate or aluminum foil, and compare it with the data before unimaginas to obtain the fabricization volatilization characteristics of the sample.
Operation steps:
01. The preliminary preparation of the sample;
02. Open the high, low -temperature bath tank and reach the set temperature;03,,,,,,,,,,,,, Clean the foggy cup and fog glass plate;
04. Place the sample;
05. Place the fog glass board or aluminum foil;
06. Place the cooling cavity;
07, the two grooves keep the set temperature and run normally to the test requirements;
08. Remove the glass plate or aluminum foil and put it until the specified time;
09 09 , Measure the weight of the gloss, fog or aluminum foil of the glass plate;10. Compare the data and get the results.
The atomization tester is an experimental equipment independently developed and produced by our company Shanghai QINSUN Precision Electrical Technology Co., Ltd., with high cost performance and complete after -sales. There are three main types of testing. Misty method and weight method.
A) Global Method:
The gas condensed on the low -temperature glass plate by the sample of the sample in the foggy cup, by the gloss value before and after the glass plate condensate, Compared with and calculated, you can get the fog value of the sample.
B) Misty method:
The sample of the samples in the fog cup is condensed on the low -temperature glass plate, and by the fog value before and after the glass plate condensate Compared with and calculated, you can get the fog value of the sample.
C) Weight method:
The gas condensed on the low -temperature aluminum foil that the sample was heated in the foggy cup, which can be obtained by weighing the weight before and after the aluminum foil condensation. The weight of the sample fog -condensate.